Laser printing method and device for implementing said method

ABSTRACT

A method for printing uses at least one ink. The method includes: a step of focusing a laser beam so as to generate a cavity in an ink film; a step of forming at least one ink droplet from a free surface of the ink film; and a step of depositing the droplet onto a depositing surface of a receiving substrate positioned at a given distance from the film. The laser beam is oriented in the direction opposite the gravitational force. The free surface of the film is oriented upwards towards the depositing surface placed above the ink film.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a National Phase Entry of International Patent Application No. PCT/FR2015/053569, filed on Dec. 17, 2015, which claims priority to French Patent Application Serial No. 1462568, filed on Dec. 17, 2014, both of which are incorporated by reference herein.

BACKGROUND AND SUMMARY

The present invention relates to a method for laser printing and to a device for the implementation thereof.

Ink printing is used in many fields to reproduce complex designs. The printing of elements can thus notably be implemented in fields as varied as biology, electronics, materials or clockmaking. The problems met in these fields are similar and relate in particular to needs for making elements combinations on a very small scale. A reproduction of patterns which consists in depositing material at specific locations can be chemically or physically performed by using masks or resorting to a step of selective ablation.

To overcome the disadvantages of these methods (risk of contamination, complex implementation, difficult combination of the deposition of several elements), ink printing methods have been developed. These have the advantage of being adapted to very freely generate element patterns using computer-aided design tools which they are associated with.

In the field of biology, depending on the works, such printing methods are called bio-printing, micro-printing of biological elements or simply bio-printing. According to these methods, the biological tissue is obtained by printing droplets of bio-inks. In order to reach some volume, the droplets are arranged in layers which are stacked on each other.

In a first embodiment, ink is stored in a tank and goes through nozzles or capillaries in order to form droplets that are transferred onto a substrate. This first alternative solution, so-called a nozzle printing includes bio-extrusion, ink-jet printing or micro-valves printing. Bio-extrusion makes it possible to obtain a significant cell density of the order of 100 million cells per milliliter and a resolution of one millimeter. Micro-valves printing makes it possible to obtain a lesser cell density of the order of several million cells per milliliter and a better resolution of the order of 100 μm. Ink-jet printing makes it possible to obtain a cell density identical with that of micro-valves printing, of less than 10 million cells per milliliter and a better resolution of the order of 10 μm.

In the case of bio-extrusion, the cells are deposited from a first nozzle and a hydrogel is simultaneously deposited from a second nozzle. As an alternative solution, the cells and the hydrogel are mixed in a tank prior to the extrusion. In the two other cases, ink is an aqueous medium containing the cells. According to the alternative solutions, bio-extrusion makes it possible to deposit the ink continuously as filaments or discontinuously as droplets.

According to such nozzle printing modes, as the printing resolution is linked in particular to the nozzle section, only bio-inks with given rheological characteristics can be used for high resolutions. Bio-inks with high cell density can thus be printed with difficulty, with a high resolution since such printing technique induces, upon the passage of ink through the nozzle, high shear stresses liable to damage the cells. Besides, with this type of ink, the risk of nozzles being blocked by the cells is important mainly because of the sedimentation of cells inside the tanks.

A method for printing biological elements by laser has been developed in order to be able to use a wide range of bio-inks and achieve high resolution. This printing method, called laser bio-printing, is also known as “Laser-Assisted Bio-printing” (LAB). The invention specifically relates to this type of printing methods. For comparison, bio-laser printing makes it possible to print inks with a high cell density of the order of 100 million cells per milliliter with a resolution of 10 μm. Similarly, laser printing has also been developed in other fields in order to improve resolution and expand the range of usable inks.

Compared to the nozzle printing techniques, laser printing provides greater flexibility in use (ability to print on soft, uneven surfaces . . . ), reduces shear stress, and limits the risk of settling. According to another advantage, it is possible to print from a small volume of ink of the order of a few microliters, which is interesting for deposits of expensive materials. Eventually, it is possible to use the printing system to view and select the drop region as described in WO2011/107599.

As illustrated in FIG. 1, a device for laser printing biological elements which is based on the so-called “Laser-Induced Forward Transfer” (LIFT) technique, comprises a pulsed laser source 10 emitting a laser beam 12, a system 14 for focusing and orienting the laser beam 12, a donor substrate 16 which comprises at least one bio-ink 18 and a receiving substrate 20 so positioned as to receive droplets 22 emitted from the donor substrate 16. According to this printing technique, the laser beam is pulsed and a droplet is generated on each pulse.

Bio-ink 18 comprises a matrix, for example an aqueous medium, wherein elements are present, for example, cells, to be deposited onto the receiving substrate 20. The donor substrate 16 comprises a blade 24 transparent to the wavelength of the laser beam 12 which is coated with an absorbent layer 26 whereon bio-ink 18 is affixed as a film. The absorbent layer 26 makes it possible to convert light energy into kinetic energy. The laser beam 12 thus produces a punctual heating at the absorbent layer 26 that generates, by vaporization, a gas bubble 28 which, by expansion, causes the ejection of a droplet 30 of bio-ink.

According to a known arrangement, the laser beam 12 impacts the donor substrate 16 by being oriented in an approximately vertical direction and in an upward direction, or in the same direction as the gravitational force G. Bio-ink 18 is thus placed under the blade 24 so as to be oriented downwards, towards the receiving substrate 20 which is placed under the donor substrate 16. Given this arrangement, bio-ink 18 is in the form of a film with a thickness E lower than a given threshold to be held on the blade. This threshold varies in particular according to the surface tension, viscosity and density of bio-ink.

The formation of droplets 30 from the ink film depends on many parameters which relate in particular to the laser beam 12 (wavelength, energy, pulse duration, . . . ), the nature of the bio-ink 18 (surface tension, viscosity, . . . ), to external conditions (temperature, humidity, . . . ). The formation of droplets 30 also depends on the thickness E of the bio-ink film. The droplets will not form if the thickness E of the bio-ink film is not included in a thickness range defined by a lower bound and an upper bound. If the thickness E has a value above the upper limit, no droplet will form because the expansion of the gas bubble 28 is too weak to reach the free surface of the film. If the thickness E has a value under the lower limit, the gas bubble will burst 28 at the free surface causing the uncontrolled projection of a plurality of micro-droplets toward the receiving substrate.

Therefore, the film thickness E has to be substantially constant over the entire surface of the donor substrate 16 to obtain reproducibility of the droplet formation whatever the region of the donor substrate 16 affected by the laser beam 12. Now, as illustrated in FIG. 1, this thickness E is not constant. This reproducibility issue is not limited to the case of bio-inks. It is present whatever the field of use, during the laser printing of an ink film.

To remedy this problem, a publication entitled “Microdroplet deposition through a film-free laser forward technique” published on Oct. 1, 2011 on the site www.elsevier.com provides for a device as described in FIG. 2. As before, this device comprises a laser source 32 emitting a laser beam 34, a system 36 for focusing and orienting the laser beam 34, a donor substrate 38 which contains at least one bio-ink 40 and a receiving substrate 42 positioned to receive droplets 44 emitted from the donor substrate 38. According to this publication, the donor substrate 38 includes a tank 46 with no upper wall so that the free surface 48 of the bio-ink 40 contained in the tank faces the receiving substrate 42. To obtain a regular, substantially planar, free surface 48 bio-ink is not a thin film but a volume having a depth of the order of 3 mm. Thus, the tank bottom has no influence on the shape of the free surface 48 of the bio-ink and the side walls of the tank have a limited effect at the periphery of the free surface 48 because of the surface tension.

Given the depth of the volume of bio-ink, the free surface 48 is necessarily directed upwards to stay in the tank and the receiving substrate 42 is positioned above the bio-ink 40. According to this document, to obtain the ejection of a droplet, the laser beam 34 is focused just below the free surface 48 and has a depth of the order of 40 to 80 μm. Thus, the droplets emitted from the free surface 48 are projected toward the receiving substrate 42 in a direction of movement opposite the direction of the gravitational force G.

Although the solution proposed by this publication makes it possible to obtain a flat free surface 48 for the ink, it is not necessarily adapted to inks in the form of suspensions, such as bio-inks. As a matter of fact, as indicated above, such bio-inks contain elements to be printed, such as, for instance cells, embedded in a matrix, which tend to settle down on the tank bottom. As the concentration in elements to be printed is low near the free surface, the printed droplets have de facto low concentrations in cells, which is generally detrimental to the printed biological tissue. Besides, according to this method, the number of cells and the concentration in deposited cells can hardly be controlled.

Such settlement issue is not limited to bio-inks. Thus, it is found during the laser printing of inks as suspensions, such as suspensions of particles or nanoparticles in a liquid matrix, whatever the field of application of such inks. According to another disadvantage of the method of the publication, the ink must be able to absorb the laser beam, which could limit the range of inks that can be printed using this technique.

The present invention therefore aims to remedy the drawbacks of the prior art by providing a printing method which makes it possible to print a wide range of elements with great accuracy. In particular, this method makes it possible to print a wide range of biological elements, specifically so as to obtain complex biological tissues. For this purpose, the invention relates to a method for printing with at least one ink, with said method comprising a step of focusing a laser beam so as to generate a cavity in an ink film, a step of forming at least one ink droplet from a free surface of the ink film and a step of depositing said droplet onto a depositing surface of a receiving substrate positioned at a given distance from the film, characterized in that the laser beam is oriented in the direction opposite the gravitational force, with the free surface of the film being oriented upwards towards the depositing surface placed over the ink film.

This configuration makes it possible, in particular, to obtain a substantially constant thickness E for the ink film, while limiting the occurrence of settling phenomena. Besides, it makes it possible to use a wide range of inks. The ink printed using the method according to the invention can be any liquid ink and can be a solution or a suspension.

Bio-inks, the inks used in electronics or watchmaking can be cited, among the usable inks. According to one application, the ink is a bio-ink.

According to another characteristic, the film has a thickness of less than 500 μm and/or has a dimension of the free surface of the film on film thickness ratio greater than or equal to 10. The distance separating the ink film and the depositing surface and/or the beam laser energy are preferably so adjusted that the kinetic energy of the droplet is almost equal to zero when the droplet contacts the depositing surface. Such characteristic limits the risks of damaging the elements (cells or other elements) contained in the droplet. According to one embodiment, the distance separating the ink film and the depositing surface is equal to 1 to 2 mm and the beam laser energy is so adjusted that the kinetic energy of the droplet is almost equal to zero when the droplet contacts the depositing surface.

According to another characteristic, the printing method comprises a preliminary phase of calibration of the laser beam energy. This calibration phase comprises a step of measuring an included angle of a deformation of the free surface of the ink film at a set time after the impact of the laser beam and a step of adjusting the laser beam energy as a function of the measured value of the included angle.

The laser beam energy is so adjusted that the included angle is less than or equal to 105°. In this case, the laser beam energy is sufficient to cause the formation of a droplet. The energy of the laser beam is advantageously so adjusted that the included angle is greater than or equal to a second threshold to obtain a kinetic energy almost equal to zero at the time when the formed droplet reaches the depositing surface.

For an ink, preferably a biological ink, film with a thickness of the order of 40 and 50 μm, the time for measuring the included angle is preferably of the order of 4 to 5 μs from the impact of the laser beam. Advantageously, the ink film has a thickness greater than 20 μm. For an ink which is in suspension with a high concentration in elements to be printed, the ink film preferably has a thickness ranging from 40 to 60 μm. Advantageously, in order to improve the accuracy of the deposition of the elements to be printed, the ink film 74 has a thickness E between 1.5D and 2D, with D being the diameter of the elements to be printed which have an approximately spherical shape or the diameter of a sphere in which at least one element to be printed is inscribed.

The invention also relates to a printing device for implementing the printing method of the invention. It comprises:

at least a pulsed laser source so configured as to emit a laser beam,

an optical system for focusing and orienting said laser beam,

at least one donor substrate which at least an ink film is attached to with a free surface, and

at least one receiving substrate comprising a depositing surface.

The printing device is characterized in that the laser beam is oriented in the direction opposite the gravitational force and in that the free surface of the film is oriented upwards towards the depositing surface placed above the ink film.

BRIEF DESCRIPTION OF THE DRAWINGS

Other characteristics and advantages will appear from the following description of the invention, and such description is given by way of example only, with reference to the appended drawings in which:

FIG. 1 is a schematic representation of a laser printing device which illustrates an alternative solution of the prior art;

FIG. 2 is a schematic representation of a laser printing device which illustrates another alternative solution of the invention;

FIG. 3 is a schematic representation of a laser printing device which illustrates the invention;

FIGS. 4A to 4D are side views illustrating the formation or not of a droplet according to different rates;

FIGS. 5A to 5D are diagrams illustrating a droplet at different times of its formation, with the last FIG. 5D illustrating the time when a droplet reaches a receiving substrate;

FIG. 6 is a section of a donor substrate illustrating the relationship between the size of the elements to be printed and the thickness of a bio-ink film;

FIGS. 7A and 7B are side views illustrating the formation of a protrusion on the free surface of a bio-ink film prior to the formation of a droplet, produced at the same time but with different energies for the laser beam;

FIG. 8 is a schematic representation of a printing device according to one embodiment of the invention which combines at least one laser-type print head and at least one ink-jet-type print head;

FIG. 9 is a perspective view of a printing device according to one embodiment of the invention which combines a laser-type print head and several ink-jet-type print heads;

FIG. 10 is a perspective view of a part of the printing device of FIG. 9 when printing with an ink-jet-type print head;

FIG. 11 is a sectional view of a part of the printing device of FIG. 9 when printing with an laser-type print head;

FIG. 12 is a perspective view of a 3-dimensional representation of a portion of a biological tissue which is to be replicated;

FIG. 13 is a perspective view of a slice of the representation of FIG. 12; and

FIG. 14 is a top view of the slice of FIG. 13 illustrating the positioning of the bio-inks droplets.

DETAILED DESCRIPTION

FIG. 3 shows a printing device 50 for producing at least one biological tissue through a layer by layer assembling according to a predefined arrangement, of various components such as an extracellular matrix and various morphogens. Thus, the printing device 50 makes it possible to deposit, layer by layer, droplets 52 of at least one bio-ink 54 onto a depositing surface 56 which corresponds to the surface of a receiving substrate 58 for the first layer or for the last layer deposited on said receiving substrate 58 for the following layers. In order to simplify the representation, the depositing surface 56 corresponds to the surface of the receiving substrate 58 in FIG. 3.

According to one embodiment in FIG. 6, the bio-ink 54 comprises a matrix 60, for example an aqueous medium, wherein elements 62, for example, cells or cell aggregates, to be printed onto the depositing surface 56 can be found. As the case may be, a bio-ink 54 comprises, in the matrix 60, only one kind of elements to be printed 62 or several kinds of elements to be printed 62. In an alternative solution, the bio-ink 54 may comprise one component only.

Bio-ink means, for the present patent application, a biological material or bio-material. For example, the bio-ink only comprises an extracellular matrix (for instance collagen), an extracellular matrix and elements such as cells or cell aggregates, an aqueous medium containing elements such as cells or cell aggregates. The bio-ink 54 is not further described because it can have different types and different rheological characteristics from one ink to another.

This printing device comprises a laser source 64 so configured as to emit a laser beam 66 which is characterized specifically by its wavelength, its frequency, its energy, its diameter, its pulse duration. Preferably, the laser source 64 can be so configured as to adjust at least one characteristic of the laser beam, in particular the energy thereof.

In order to form droplets separated from each other, the laser source 64 is a pulsed source. To give an order of magnitude, 10,000 droplets can be ejected per second. For example, the laser source 64 is a laser source with a wavelength of 1,064 nm.

In addition to the laser source, the printing device 50 includes an optical system 68 which enables the adjustment of the focus along a Z axis perpendicular to the depositing surface 56. The optical system 68 advantageously includes a lens which makes it possible to focus the laser beam 66 onto an impacted area. The optical system 68 preferably includes a mirror to change the position of the impacted area. The optical system 68 thus makes it possible to change the area impacted by the laser beam in an impact plane referenced Pi in FIG. 3. The laser source 64 and the optical system 68 are not further described either, since they are known to the persons skilled in the art and may be identical with those of the prior art.

The printing device 50 also comprises at least one donor substrate 70 which comprises, according to one embodiment, an absorbent layer 72 for the wavelength of the laser beam 66 whereon a film 74 of at least one bio-ink is affixed. In the following part of the description, film means that the bio-ink occupies a volume with a thickness (the dimension in a direction perpendicular to the plane of impact Pi) of less than 500 μm. Unlike a tank, the fact that bio-ink is packaged as a film can make it possible to avoid settling phenomena.

The absorbent layer 72 is made of a material adapted to the wavelength of the laser beam 66 to transform the light energy into a punctual heating of the absorbent layer 72. The donor substrate 70 is preferably so positioned that the optical system focuses the laser beam at the absorbent layer 72. According to one embodiment, the absorbent layer 72 is made of gold, titanium, or another component according to the wavelength of the laser beam 66. According to another embodiment, the donor substrate 70 includes no absorbent layer 72. In this case, the laser beam 66 energy is absorbed by the ink.

The donor substrate 70 preferably comprises a blade 76 made of a material transparent for the wavelength of the laser beam 66 which includes, on one of its faces, a coating corresponding to the absorbent layer 72. The presence of the blade 76 imparts stiffness to the donor substrate 70 which makes it possible to handle and keep the ink and/or the absorbent layer 72 substantially flat in the impact plane Pi. The bio-ink film 74 comprises a free surface 78 which is spaced from the absorbent layer 72 by a distance E corresponding to the thickness of the film 74 and which is spaced from the depositing surface 56 by a distance L. The free surface 78 and the depositing surface 56 face each other. As illustrated in FIG. 3, the laser beam 66 is adapted to produce a cavity 80 at the interface between the absorbent layer and the bio-ink film 74 which generates a droplet 82 which detaches from the free surface 78 to move to the depositing surface 56.

In the following part of the description, a vertical direction is parallel to the gravitational force G and the up-down direction corresponds to the direction of the gravitational force G. The direction of the laser beam 66 and the direction of the droplet movement are parallel to the vertical direction.

Upward Printing:

According to one characteristic of the invention, the laser beam 66 and thus the movement of the droplet 82 are oriented in the opposite direction relative to the gravitational force G. The free surface 78 of the bio-ink film 74 is thus directed upwards. When moving from the bio-ink film 74 to the depositing surface 56, the droplet 82 moves upwards in the down-up direction.

This configuration provides the following advantages:

It limits the occurrence of settling phenomena, with the bio-ink being in the form of a film,

It makes it possible to obtain a substantially constant thickness E for the bio-ink film 74, with the influence of the gravitational force G on the shape of the free surface 78 of the film 74 being limited by the free surface 78 being oriented upward,

It makes it possible to use a wide range of bio-ink when an independent absorbent layer 72 of the bio-ink film 74 is used to transform the light energy into a punctual heating.

Almost Aero Kinetic Energy at the Time of Depositing a Droplet onto the Receiving Substrate:

The formation of a droplet 82 from a bio-ink film will depend on many parameters, mainly the characteristics of the bio-ink, the characteristics of the laser beam and the conditions of implementation. FIGS. 4A to 4D show the evolution during the time of deformation of the free surface of the bio-ink film, which results, or not, in the formation of a droplet, for different values of the beam laser 66 energy, with the latter having an energy of 21 μJ in FIG. 4A, 35 μJ in FIG. 4B, 40 μJ in FIG. 4C and 43 μJ in FIG. 4D.

For the same bio-ink and under the same embodiment conditions, it can be noted that several rates exist, according to the energy of the laser beam. As illustrated in FIG. 4A, if the energy of the laser beam is less than a lower threshold, the droplet does not detach from the bio-ink film 74. Since the maximum height of the deformation 84 generated at the free surface 78 of the ink film 74 is less than the distance L between the film 74 and the depositing surface 56, no element is printed. According to the selected example, the lower threshold ranges from 21 μJ to 35 μJ. As illustrated in FIG. 4D, if the energy of the laser beam is above an upper threshold, the gas bubble 80 produced inside the film breaks at the free surface thus causing the uncontrolled projection of microdroplets. According to the selected example, the upper threshold ranges from 40 μJ to 43 μJ.

Between the lower and upper thresholds, as illustrated in FIGS. 4B and 4C, the rate is such that it enables the formation of a jet. If the distance L separating the film 74 and the depositing surface 56 is sufficient, this rate enables the formation of a droplet. Preferably, the distance L is of the order of 1 to 2 mm to enable the formation of a droplet and not of a continuous jet which stretches out from the film up to the depositing surface. This configuration limits the risks of contamination of the biological tissue achieved by the bio-ink.

According to another characteristic of the invention, for the same bio-ink and under the same embodiment conditions, the distance L separating the ink film 74 and the depositing surface 56 and/or the beam laser 66 energy are so adjusted that the kinetic energy of the droplet is almost equal to zero when the droplet 82 contacts the depositing surface 56, as illustrated in FIG. 5D. This configuration limits the risk of damaging the elements to be printed which are cells. Almost equal to zero means that the kinetic energy is null or slightly positive to enable the droplet to settle down on the depositing surface 56. This circumstance is made possible because the droplet 82 moves in the opposite direction relative to the gravitational force G.

The distance L separating the bio-ink film 74 and the depositing surface 56 is preferably stationary. Thus, the laser beam 66 energy is so adjusted that the kinetic energy of the droplet is almost equal to zero when the droplet 82 contacts the depositing surface 56. Whatever the application, printing with a rate which leads to a deposit at zero speed reduces the risks of the droplet splashing when contacting the depositing surface.

Calibration Technique:

As indicated above, the formation of the droplet is not related to the energy of the laser beam only. It is also related to the nature of the bio-ink especially the viscosity, the surface tension and the conditions of implementation thereof.

FIGS. 5A to 5D, 7A to 7D illustrate a calibration method for determining the energy of the laser beam for obtaining an optimal rate for the formation and the deposition of droplets, specifically a rate that leads to a deposit at zero speed at a given distance L. FIGS. 5A to 5D show some of the steps of forming a droplet 82 between the time of impact of the laser beam shown in FIG. 5A and the deposition of the droplet 82 on the depositing surface 56. According to one characteristic of the invention, the calibration method for adjusting the laser energy comprises the steps of measuring an included angle θ of a deformation 86 of the free surface 78 of the film 74 of the bio-ink at a set time T1 after the impact of the laser beam 66 and of adjusting the energy of the laser beam 66 according to the measured value of the included angle θ.

As illustrated in FIGS. 5B, 7A and 7B, the deformation 86 has a symmetrical shape with respect to a median axis Am parallel to the vertical direction. This deformation 86 includes a vertex S centered on the median axis Am. This vertex S corresponds to the deformation area 86 furthest from the rest of the free surface 78 of the film 74.

In a plane containing the median axis Am, the vertex S is extended by a first flank 88 on one side of the median axis Am and by a second flank 88′ on the other side of the median axis Am, with both flanks 88, 88′ being symmetrical with respect to the median axis Am. Each face 88, 88′ comprises a point of inflexion. The first flank 88 comprises a first tangent Tg1 at its inflexion point and the second flank 88 includes a second tangent Tg2 at its inflexion point, with the two tangents Tg1 and Tg2 being secant at a point of the median axis Am.

The included angle θ corresponds to the angle formed by the tangents Tg1 and Tg2 and facing the film 74 (or downwards). For the formation of a droplet, the included angle θ must be smaller than or equal to a first threshold θ1. As illustrated in FIG. 7A, if the included angle θ is above the first threshold θ1, the energy of the laser beam is thus not sufficient to generate a droplet. On the contrary, as shown in FIG. 7B, if the included angle θ is smaller than the first threshold θ1, the laser beam energy is sufficient to generate a droplet.

To obtain a near-zero kinetic energy when the formed droplet reaches the depositing surface 56 at a distance L from the free surface 78 of the film 74, the included angle θ must be greater than or equal to a second threshold θ2. The value of the included angle θ is preferably determined using a take at the time T1 of the deformation 86. In one embodiment, the take is performed using a camera, the axis of sight of which is perpendicular to the vertical direction.

The time T1 advantageously depends on the film thickness and very little varies from one ink to another. The time T1 is advantageously of the order of 4 to 5 μs from the impact of the laser beam for a thickness E of the film of the order of 40 to 50 μm. This time T1 is illustrated in FIG. 5B.

The first threshold θ1 is approximately equal to 105°. Thus, if at the time T1 the included angle θ is less than or equal to 105°, the laser beam energy is sufficient to generate a droplet 82. The second threshold 02 depends on the distance L between the depositing surface 56 and the free surface 78 of the ink film 74. The second threshold θ2 is inversely proportional to the distance L.

The second threshold θ2 is high and equal to approximately 80° for a small distance L, of the order of 1 mm. A relatively small distance L will be preferred to reduce the stresses in the jet and at the time of the contact of the droplets with the depositing surface. The second threshold θ2 is low and equal to approximately 50° for a substantial distance L of the order of 10 mm. A relatively long distance L will be preferred if a remote printing is desired, for instance, if the donor substrate 70 has larger dimensions than those of the well at the bottom of which the depositing surface 56 is positioned. This technique for calibrating the laser beam energy makes it possible to optimize the speed of the jet by reducing it in order to limit the risks of damaging the elements contained in the ink particularly at the time of deposition on the depositing surface 56.

Thickness of the Ink Film:

The bio-ink composition preferably includes a high concentration in elements to be printed 62 in order to obtain a biological tissue with a high concentration in cells. In this case, as illustrated in FIG. 3, the droplet 82 includes a volume fraction with a high concentration in elements to be printed 62.

For bio-inks with a high concentration, the thickness E of the film 74 is of the order of 40 to 60 μm. In order to improve the accuracy of the deposition of the elements to be printed, the film 74 of bio-ink advantageously has a thickness E ranging from 1.5D to 2D, with D being the diameter of the elements to be printed 62 which have an approximately spherical shape or the diameter of a sphere wherein an element to be printed 62 is inscribed. According to one embodiment, the bio-ink film 74 has a thickness E greater than or equal to 20 μm for smaller elements to be printed which have a diameter of the order of 10 to 15 μm. The thickness E of the film may be of the order of 400 μm when the elements to be printed 62 are aggregates of cells. Generally, the thickness E of the film is less than 100 μm when the elements to be printed 62 are unit cells.

Preferably, the film 74 is characterized by a (dimension of the free surface 78)/film thickness 74) ratio greater than or equal to 10, and advantageously greater than or equal to 20. The size of the free surface 78 corresponds to the largest dimension of the free surface 78 of the film 74 in a plane parallel to the plane of impact Pi.

Printing Technique Combining a Laser-Type Print Head and a Nozzle Print Head:

According to another characteristic of the invention, the printing method uses at least one laser-type print head for at least a first bio-ink and at least one nozzle print head for at least a second bio-ink. This combination makes it possible to increase the production rate. Nozzle print head means a print head which comprises an orifice through which the second bio-ink passes. Thus, a nozzle print head may be a print head of the ink-jet type, a microvalves print head, a print head of the bio-extrusion type.

Each print head of the laser type is preferably the same as the one described in FIG. 3. However, the invention is not limited to this type of laser print head. Using laser-type print heads as described in FIGS. 1 and 2 or other print heads can be considered. The nozzle print heads are not described any further since they are preferably identical with those of the prior art. In the case of a biological tissue comprising disjoint cells separated by extracellular materials, the extracellular materials are preferably deposited by the nozzle print head(s) and the cells are preferably deposited by the laser-type print head(s).

As the extracellular materials are less sensitive to shear effects, they can be deposited using a nozzle print head. As the bio-ink cartridges intended for the nozzle print heads have a very much higher volume than the volume of ink (of the order of 40 μm) supported by a donor substrate 70 intended for a laser-type print head, the materials of the extracellular matrix can be deposited with a high flow rate. Although a nozzle print head is capable of depositing inks with a high flow rate, as each donor substrate intended for a laser type print head supports a very small volume of ink, it is necessary to change these frequently, which tends to increase the removal time relative to a nozzle print head.

According to another characteristic, the laser type head(s) or printing and the nozzle print head(s) are integrated in the same machine and move in the same coordinate system. This configuration makes it possible to simplify the relative positioning of the various print heads, to improve the accuracy of the removal and to guarantee the integrity of the printed elements.

Printing Device Comprising a Donor Substrates Storage Chamber:

FIGS. 8 to 11 show a printing device according to one embodiment of the invention. The printing device 100 includes a chassis supporting a print head 102 of the laser type and several print heads 104, 104′, 104″ of the ink-jet type. The chassis 100 includes a coordinate system X, Y, Z, with the Z axis being oriented in the vertical direction, and with the X, Y plane corresponding to a horizontal plane.

The print heads 102, 104, 104′, 104″ are stationary with respect to the chassis 100 and so positioned that the droplets are emitted vertically upwards. The print heads 102, 104, 104′, 104″ are offset in a first direction parallel to the Y axis. In one embodiment, the print heads 104, 104′, 104″ of the ink-jet type are joined together. The print head 102 of the laser type is spaced from the print heads 104, 104′, 104″ of the ink-jet type.

The printing device also comprises a mobile chassis 106, a system for guiding and moving the mobile chassis 106 relative to the chassis 100 in three directions parallel to the X, Y, Z axes and a control system for controlling the displacements of the mobile chassis 106. The guide and displacement system and the control system are so selected as to achieve a micrometric precision as regards the movements of the mobile chassis 106 relative to the chassis.

As illustrated in FIG. 10, the mobile chassis 106 includes a frame 108 for releasably attaching at least one receiving substrate 58. When it is secured to the mobile chassis, the movements of the receiving substrate 58 are controlled with micrometric precision. The print head 102 of the laser type comprises a hollow cylindrical body 110, stationary relative to the chassis, which contains a part of an optical system and whereon a tubular portion 112 is positioned which includes an upper end 114 which opens into a horizontal plane. These elements are so configured that a laser beam guided by the optical system scans the section of the upper end 114.

Each donor substrate 70 has the shape of a disk positioned on a base 116. According to one embodiment illustrated in FIG. 11, each base 116 has the shape of a tube which comprises, at its upper edge, a recess 118 which has a diameter identical to that of a donor substrate 70 and a height sufficient to hold same. This recess 118 thus makes it possible to position a donor substrate 70 relative to the base which supports same.

The upper end 114 and the base 116 have shapes that cooperate with each other so that the base 116 is immobilized in a given position relative to the upper end 114 and thus with respect to the X, Y, Z system of the chassis. According to one embodiment, the base 116 includes an outer flange 120 which bears against the upper end 114 and makes it possible to position the base along the Z axis. Under the flange 120, the base 116 includes a frustoconical surface 122 which cooperates with a tapered portion provided inside the tubular portion 112. These shapes make it possible to center the base 116 relative to the tubular portion 112 and to position same in an XY plane. Magnetic materials can preferably be used to improve the positioning of the base 116 relative to the tubular portion 112.

The printing device 124 advantageously comprises a chamber so configured as to store at least one base 116. The chamber 124 comprises at least one opening 125 for inputting and outputting the stored bases 116. According to one embodiment, the chamber 124 has a parallelepiped shape. The chamber 124 preferably has dimensions adapted to store several bases. The printing device can thus successively print several bio-inks with the same print head 102 of the laser type.

The bases 116 are stored on a base plate 126 which comprises recesses 128, i.e. one recess for each base 116. The base plate 126 has an elongated shape and comprises, on its whole length, U-shaped notches 128. According to a first alternative solution illustrated in FIG. 9, the length of the base plate 126 is oriented along the Y axis.

According to a second preferred embodiment, the length of the base plate 126 is oriented along the X axis and the notches 128 are open towards the print heads. The chamber 124 advantageously includes, on a first side facing the print heads, a first opening 125 enabling the bases 116 to come out and, on another side, a second opening 125′ for introducing the bases 116.

According to one embodiment, the chamber 124 includes a guide system for positioning the base plate 126, for example a rail, with the base plate 126 comprising, in the lower part, a groove the cross-section of which engages with that of the rail. This rail opens at the second opening 125′. It is preferably oriented along the X axis.

The chamber 124 comprises containment means for preserving, inside the chamber, an atmosphere adapted to bio-inks, in particular as regards temperature and/or hygrometry. Such containment means are provided in particular at each opening 125, 125′. They may take the form of a barrier or an air curtain.

In addition to the chamber, the printing device includes a mobile clamp 130 to move the bases between the chamber 124 and the print head 102 of the laser type. In a first alternative solution, the mobile clamp 130 is secured to a mobile carriage 132, independent of the mobile chassis 106, which is configured to move in the X, Y, Z directions. According to another alternative solution, the mobile clamp 130 is secured to the mobile chassis 106.

According to one embodiment, the printing device includes a shooting device (not shown) the line of sight of which is perpendicular to the vertical direction and faces the upper surface of the donor substrate. This device can be used to calibrate the energy of the laser beam of the print head 102 of the laser type.

Method for Producing a Biological Tissue using Bio-Printing:

The first step of said method consists in generating a three-dimensional digital representation of the biological tissue to be printed. In FIG. 12, a portion of such a representation is shown (140) as a cube which has a first volume region 142 positioned inside within a second volume region 144 itself positioned in a third volume region 146. For the purpose of the description, the representation 140 is greatly simplified.

Each volume region 142, 144, 146 is colored or textured differently, with each color or texture corresponding to a set of characteristics among the following (not limited) ones: material, manufacturing means, trajectory, . . . Each color or texture preferably corresponds to a bio-ink. All the volume regions 142, 144 and 146 are closed.

The representation advantageously comprises a plurality of small elementary volumes which have different colors or textures depending on the volume region which they belong to. According to one embodiment, the representation 140 originates from a computer file of the PLY type.

The second step of the method consists in slicing the representation 140 into a succession of stacked layers along an axis Z. In FIG. 13, a layer 148 of the 140 representation has been separated. When slicing the representation 140, in line with a change of volume region, each layer comprises an edge which corresponds to a new region.

As illustrated in FIG. 13, the layer 148 comprises a first region 142′ which corresponds to the first volume region 142, a second region 144′ which corresponds to the second volume region 144 and a third region 146′ which corresponds to the third volume region 146. For each layer, the regions 142′, 144′, 146′ are colored or textured according to the color or texture of the volume regions 142, 144, 146.

Each layer has a thickness c which is determined according to the height of the printed droplets. If the layer comprises only one material to be printed, the layer has a thickness substantially equal to the height of a droplet. When the layer comprises several materials to be printed, in a first alternative solution, the layer has a thickness equal to the lowest common multiple of the heights of the droplets associated with each material. This alternative solution has the advantage of minimizing any shifting on the whole height of the object to be printed and to achieve fast printing.

According to a second alternative solution, the layer has a thickness equal to the highest common factor of the heights of the droplets associated with each material. This alternative solution has the advantage of increasing the resolution and the number of layers.

For example, if the first material is printed by laser bio-printing, the printed droplets have a height of the order of 10 μm. If the second material is printed using micro-valves bio-printing, the printed droplets have a height of the order of 100 μm. In the first alternative solution, the layers have a thickness of the order of 100 μm. In the second alternative solution, the layers have a thickness of the order of 10 μm. Preferably, each layer comprises a plurality of small elementary, for example triangular, polygons which have different colors according to the region which they belong to. The object to be printed thus corresponds to a set of layers which each comprise a set of polygons, each having an associated color or texture.

A third step of the method consists in determining, for each layer, the position of the droplets to be printed of each bio-ink according to the colored or textured regions 142′, 144′, 146′ and the expected volume of each droplet. For this purpose, each region 142′, 144′, 146′ of each layer is filled with ellipses 142″, 144″, 146″, the dimensions of which depend on the dimensions of the droplets of the bio-ink to be printed in said region, as shown in FIG. 14.

For each region, the ellipses have the same dimensions. All the ellipses have parallel focal axes. The elliptical shape makes it possible to adjust the distances between the droplets in two directions (a first direction parallel to the focal axes and a second direction perpendicular to the first one). The center of each ellipse corresponds to the position of the center of a droplet. The ellipses are positioned region by region, in the descending order of sizes, thus the larger ellipses arranged in the region 146′ are positioned first and the smaller ellipses arranged in the region 142′ are positioned last.

Preferably at a region change, the positioning is optimized according to two criteria:

the maximum ratio of elementary polygons having the right color or texture in an ellipse, of the order of 75% for example,

the minimum ratio of elementary polygons having the wrong color or texture in an ellipse, of the order of 5% for example.

Ellipses Overlapping can be Tolerated.

A fourth step of the method consists in synchronizing the movement of the depositing surface 56 whereon the bio-ink droplets are printed and the various print heads. For bio-laser printing, the laser focusing area is the center of each laser printed ellipse, and each ellipse is the subject of a laser pulse. In this case, the depositing surface is stationary, the laser scans the entire depositing surface. For a depositing surface larger than the donor substrate, the substrate can also be moved (where the depositing surfaces are tipped on) in synchronization with the laser scan.

For a nozzle bio-printing, the center of each ellipse corresponds to the assumed point of impact of a droplet on the depositing surface 56. In this case, the print nozzle is stationary, the substrate moves. However, the print nozzle may be movable.

Applications:

Bio-printing according to the invention can be used to produce:

Implantable tissues for regenerative medicine,

Individualized tissues, made from the patient's cells, making it possible to select the treatments, in vitro, and to develop customized therapeutic solutions,

Predictive models reproducing the physiology of sound human tissues or tissues affected by a pathology in order to predictively test the efficacy or the toxicity of the molecules, of ingredients and of the drug candidates.

By Way of Example and Without Limitation, the Biological Tissue is a Bone Tissue.

Although described as applied to bio-inks, the invention is not limited to this application. The method and the device according to the invention can thus be used to print any liquid ink, as a solution or a suspension. Other suitable inks include but are not limited to the inks used in electronic coatings, in materials or in watchmaking.

For example and without limitation, the inks can be composed of:

Precious (specifically gold, silver, platinum, rhodium and palladium) or semi-precious (titanium, zirconium, copper) metals,

Functional alloys,

Organic materials,

Sol-gel systems,

Ceramics or microcomposites or nanocomposites.

These different materials make it possible to produce various types of coatings:

Anticorrosive coatings,

Coatings with a high chemical resistance,

Bio-functional (antibacterial, antimicrobial, biocompatible) coatings,

Coatings for food contact,

Coatings modifying the surface energy,

Release coatings,

Electro-technical (insulating, antistatic or conductive) coatings

Wear resistant coatings

Coatings modifying the optical properties (anti-reflective, photocatalytic, IR/UV barrier),

Coatings affecting the haptic sense

Coatings for reducing the friction coefficient,

Coatings making it possible to increase durability at high temperatures. 

1. A method for printing with at least one ink, with the method comprising: focusing a laser beam so as to generate a cavity in an ink; forming at least one ink droplet from a free surface of the ink film; depositing the droplet onto a depositing surface of a receiving substrate positioned at a given distance from the film; and orienting the laser beam in a direction opposite a gravitational force, with the free surface of the film being oriented upwards towards the depositing surface placed above the ink film.
 2. A printing method according to claim 1, wherein the film has a thickness of less than 500 μm.
 3. A printing method according to claim 1 wherein: the film has a dimension of the free surface of the film on the film thickness ratio greater than or equal to
 10. 4. A printing method according to claim 1, wherein the distance separating the ink film and the depositing surface and/or the beam laser energy are so adjusted that kinetic energy of the droplet is almost equal to zero when the droplet contacts the depositing surface.
 5. A printing method according to claim 1, wherein the distance separating the ink film and the depositing surface is equal to 1 to 2 mm and energy of the laser beam is so adjusted that the kinetic energy of the droplet is almost equal to zero when the droplet contacts the depositing surface.
 6. A printing method according to claim 1, further comprising a preliminary phase of calibration of energy of the laser beam which comprises measuring an included angle of deformation of the free surface of the ink film at a set time after an impact of the laser beam, and adjusting the laser beam energy according to the measured value of the included angle.
 7. A printing method according to claim 6, wherein the laser beam energy is so adjusted that the included angle is less than or equal to 105°.
 8. A printing method according to claim 6, wherein the laser beam energy is so adjusted that the included angle is greater than or equal to a second threshold to obtain kinetic energy almost equal to zero when the formed droplet reaches the depositing surface.
 9. A printing method according to claim 8, wherein the second threshold depends on the distance between the depositing surface and the free surface of the ink film.
 10. A printing method according to claim 9, wherein the second threshold is equal to approximately 80° for the distance of an order of 1 mm.
 11. A printing method according to claim 6, wherein the included angle measuring time is of an order of 4 to 5 μs as from the impact of the laser beam.
 12. A printing method according to claim 1, wherein the ink film has a thickness greater than 20 μm.
 13. A printing method according to claim 1, wherein the ink film has a thickness ranging from 40 to 60 μm for bio-inks with a high concentration of elements to be printed.
 14. A printing method according to claim 1, wherein for a bio-ink with a low concentration of elements to be printed, the bio-ink film has a thickness ranging from 1.5D to 2D, with D being the diameter of the elements to be printed which have an approximately spherical shape, wherein the diameter of a sphere in which an element to be printed is inscribed.
 15. A printing device comprising: at least one pulsed laser source configured to emit a laser beam; at least one optic operably focusing and orienting the laser beam; at least one donor substrate to which at least an ink film is attached with a free surface; and at least one receiving substrate comprising a depositing surface placed at a given distance from the film; the laser beam being oriented in a direction opposite a gravitational force; and the free surface of the film being oriented upwards towards the depositing surface placed above the ink film. 